Buna-N Rubber Roll, 36"W x 150 ft.L x 1/32"Thick, 60A, Plain Backing Type, 200% Elongation, Black
Hover over image to magnify
#921427-7 | Pkg Qty: 1
$905.26 pkg | $905.26 ea
This item requires special shipping, additional charges may apply.
Drop Ship Item
Shipping to 60045
Technical Specifications
Key Specifications
Backing
Plain
Mfr. Part Number
BULK-RS-H60-861
Brand
E. JAMES
Pack Quantity
1
Color Family
Black
Shipping Weight
138.34 lb.
Durometer
60 A
Temperature Range (Deg. F)
-30 to 250 deg. F
Finish
Smooth
Tensile Strength
1000 psi
Item
Buna-N Roll
Thickness
1/32 in.
Length
150 ft.
Width
36 in.
Material
Buna-N
General
Abrasion Resistance
Good
Rubber Grouping
Rubber Roll
Application
Oil Resistant
Rubber Properties
Oil Resistant; Water Resistant
Chemical Resistance
Fair
Rubber Shape
Sheet
Compression Set
33 %
Shape
Roll
Density
1.5 g/cc
Standards
ASTM D2000 BF 607
Elongation
350 %
Tear Strength
20 N/mm
Grade
Standard
Thickness Tolerance
+/-0.010 in
Maximum Temperature
250 °F
Type
Commercial Grade
Minimum Temperature
-30 °F
Water Resistance
Good
Oil Resistance
Excellent
Weather Resistance
Fair
Product Description
Rubber Roll, Rubber Material Buna-N, Rubber Thickness 1/32 in, Rubber Width 36 in, Rubber Length 150 ft, Plain Backing Type, Durometer 60A, Elongation 200 Percent, Tensile Strength (PSI) 1,000 psi, Min. Temp. (F) -30 Degrees F, Max. Temp. (F) 220 Degrees F, Rubber Color Black, Smooth Finish
Item Barcode
Roll,Buna,1/32 T x36 In W,150
| Name | Item | Description | |
|---|---|---|---|
 | Grainger Dropship | 3EFX2 | Roll,Buna,1/ 32 T x36 In |
 | UNSPSC CODES | 30266402 | |
 | VMRS (ATA) CODES | 053-006-009 | Roll,Buna,1/ 32 T x36 In |
All information contained herein is the property of Imperial Supplies LLC, and is published here for your use only. Any reproduction or distribution of this information without prior written consent from Imperial Supplies LLC is strictly prohibited.
Imperial Supplies LLC does not provide services and products outside the United States
For more product information by email, click here